当前位置：首页 > 过刊浏览->2021年42卷第1期
双相不锈钢阀门铸件的裂纹缺陷分析及避免措施
Crack Defect Analysis and Preventing Measures of Duplex Stainless Steel Valve Castings
浏览(3671) 下载(20)
- DOI:
- 作者:
- 刘金旺
LIU Jinwang
- 作者单位:
- 中核四达建设监理有限公司，河北 石家庄 050000
CNNC Sida Construction Supervision Co., Ltd., Shijiazhuang 050000, China
- 关键词:
- 双相不锈钢；阀门铸件；裂纹
duplex stainless steel; valve castings; crack
- 摘要:
- 分析了双相不锈钢阀门铸件经常出现裂纹缺陷的原因。 为避免再次投产时阀门铸件裂纹缺陷的产生，制定
了相应的措施：提高砂芯的退让性；严格控制钢液的化学成分，特别是磷硫元素的含量控制；添加稀土元素细化晶粒，净
化钢液以提高抗裂性；清除浇冒口和补焊注意温度的控制。 结果表明，通过上述措施后，重新投产的阀门铸件没有裂纹
缺陷。
The causes of frequent crack defects in duplex stainless steel valve castings were analyzed. In order to avoid the occurrence of crack defects in valve casting when the valve was put into production again, the corresponding measures were formulated: improving the deformability of sand core; Strictly control the chemical composition of molten steel, especially the content of phosphorus and sulfur; Rare earth elements were added to refine grain and purify liquid steel to improve crack resistance. Clear riser and repair welding temperature control. The results show that there is no crack defect in the valve casting after the above measures.