微量稀土Ce对纯Ag组织的影响
Effect of Minor Ce on the Microstructure of Pure Ag
浏览(3368) 下载(0)
- DOI:
- 作者:
- 韩吉庆,秦涛,邹辉
- 作者单位:
- 西部金属材料股份有限公司,陕西 西安 710065
- 关键词:
- 稀土;纯Ag;组织;位错
Rareearth; Pure Ag; Microstructure; Dislocation
- 摘要:
- 系统的研究了添加微量稀土Ce对纯Ag铸态、加工态和退火态组织形貌的影响作用。对比分析了纯银和Ag0.1%Ce组织中位错在加工态和退火态的变化情况。结果表明,在Ce含量不超过0.065%时,Ag的铸态组织为单相固溶体;Ce含量过大时,组织中有Ag4Ce相析出。变形量为50%的Ag0.1%Ce合金退火后,Ag4Ce相相变的均匀。透射电镜观测表明Ag4Ce相在加工过程中对位错有阻碍作用,退火后这些位错形成晶,或扩散到晶界被吸收,或通过异号位错的作用而抵消。
The influence of minor Ce addition on the microstructures of pure Ag under ascast, coldprocessing and annealing states were systematically researched. The dislocations in the pure Ag and Ag0.1%Ce at different processing states were comparatively analyzed. The results indicated that, when the Ce content is below 0.065%, single solid solution in pure Ag was obtained under the ascast condition. As the Ce additive increases, Ag4Ce precipitate was formed. After annealing the Ag0.1%Ce alloy at 50% deformation, Ag4Ce precipitate was distributed uniformly. Transmission electron microscopy shows that Ag4Ce precipitate impeded the dislocation during the working process. The crystal formed by dislocation was whether absorbed by diffusion into the grain boundaries, or counteracted by the dislocations of minus number after annealing.